High Carbon Aluminum Clad Wire / Single Acs Lightning Protection Wire

 China High Carbon Aluminum Clad Wire / Single Acs Lightning Protection Wire supplier

High Carbon Aluminum Clad Wire / Single Acs Lightning Protection Wire image

Get a Quote Email to us

Brand Name :
Litong Global

Model Number :
LT-190521

Certification :
ISO9001,3C

Place of Origin :
Anhui,China

MOQ :
1ton

Price :
discuss

Packaging Details :
Packed in Iron Wooden Reels

Packed in Iron Wooden Reels :
Fit Customer Design

Different Grades :
14% to 40% Iacs Conductivity

Product description:

Aluminum clad steel wire is a piece of round wire made of a round steel core clad with a uniform and continuous aluminum layer. By structure ratio of steel and aluminum, aluminum clad steel wire has different grades, LB14, LB20, LB23, LB27, LB30, LB35 and LB40, with corresponding electric conductivities of 14%, 20.3%, 23%, 27%, 30%, 35% and 40% IACS (IACS stands for International Annealed Copper Standard). Featured by high strength, corrosion resistance and high conductivity, etc., aluminum clad steel wire is widely used in coastal areas, volcano areas, salt atmosphere areas and overhead power line used in areas seriously polluted by industrial materials containing SO2, NO and CO2, etc. It's the optimum material for transmission conductor with kilometric span and carrier cable for electrified railways.

Application:
Composition of Al Clad Strand Wires (ACS), Aluminum Conductors, Al Clad Steel Reinforced (ACSR/AW), OCGW,etc.

Standard:
ASTM B 415-92, ASTM B 502-93, AS 1222, IEC61232, JCS389

Parameters:

Approximate Properties of Hard-drawn 20.3% Conductivity Aluminum-Clad steel
Wire (20.3%)
Nominal Dia Size Calculated cross sectional area Min tensile
strength
Calculated
breaking
load
Mincoating
thickness
D.C resistance
at 20ºC≤

Weight

in. mm AWG mm2 cmils Mpa psi kn mm Ω/1000ft Ω/km kg/km 1b/1000ft
0.2043 5.189 4 21.150 41740 1070 155000 22.60 0.259 1.222 4.009 139.32 93.63
0.1880 4.775 4 17.908 35342 1100 160000 19.70 0.239 1.443 4.735 118.01 79.31
0.1819 4.620 5 16.767 33090 1140 165000 18.10 0.231 1.541 5.056 110.48 74.25
0.1729 4.392 5 15.150 29899 1170 170000 17.73 0.220 1.706 5.597 99.84 67.10
0.1620 4.115 6 13.296 26240 1210 175000 16.00 0.206 1.943 6.375 87.61 58.88
0.1549 3.934 6 12.155 23989 1240 180000 15.07 0.197 2.126 6.976 80.10 53.83
0.1443 3,665 7 10.549 20820 1280 185000 13.50 0.183 2.450 8.038 69.47 46.69
0.1369 3.477 7 9.495 18739 1310 190000 12.44 0.174 2.722 8.931 62.57 42.05
0.1285 3.264 8 8.366 16510 1340 195000 11.20 0.163 3.089 10.135 55.15 37.03
0.1144 2.906 9 6.633 13090 1340 195000 8.92 0.145 3.896 12.783 43.70 29.37
0.1019 2.588 10 5.260 10380 1340 195000 7.07 0.129 4.912 16.116 34.66 23.29
0.0907 2.304 11 4.170 8230 1340 195000 5.61 0.115 6.194 20.323 27.48 18.47
0.0808 2.052 12 3.309 6530 1340 195000 4.45 0.103 7.811 25.628 21.80 14.65
Approximate Properties of Hard-drawn 27% Conductivity Aluminum-Clad steel
Wire (27%)
Nominal Dia Size Calculated cross sectional area Min tensile
strength
Calculated
breaking
load
Mincoating
thickness
D.C resistance
at 20ºC≤

Weight

in. mm AWG mm2 cmils Mpa psi kn mm Ω/1000ft Ω/km kg/km 1b/1000ft
0.2043 5.189 4 21.150 41740 862 125000 18.20 0.363 0.920 3.019 124.99 84.00
0.1880 4.775 4 17.908 35342 889 129000 15.92 0.334 1.087 3.566 105.83 71.12
0.1819 4.620 5 16.767 33090 917 133000 15.40 0.323 1.161 3.809 99.09 66.59
0.1729 4.392 5 15.150 29899 945 137000 14.32 0.307 1.285 4.215 89.54 60.17
0.1620 4.115 6 13.296 26240 972 141000 12.90 0.288 1.464 4.803 78.57 52.80
0.1549 3.934 6 12.155 23989 1000 145000 12.16 0.275 1.601 5.254 71.84 48.28
0.1443 3,665 7 10.549 20820 1034 150000 10.90 0.257 1.845 6.053 62.33 41.89
0.1369 3.477 7 9.495 18739 1062 154000 10.08 0.243 2.050 6.726 56.12 37.71
0.1285 3.264 8 8.366 16510 1076 156000 9.00 0.228 2.326 7.632 49.43 33.22
0.1144 2.906 9 6.633 13090 1076 156000 7.13 0.203 2.934 9.626 39.19 26.34
0.1019 2.588 10 5.260 10380 1076 156000 5.66 0.181 3.700 12.140 31.08 20.89
0.0907 2.304 11 4.170 8230 1076 156000 4.48 0.161 4.667 15.312 24.63 16.55
0.0808 2.052 12 3.309 6530 1076 156000 3.56 0.144 5.882 19.299 19.55 13.14
Approximate Properties of Hard-drawn 30% Conductivity Aluminum-Clad steel
Wire (30%)
Nominal Dia Size Calculated cross sectional area Min tensile
strength
Calculated
breaking
load
Mincoating
thickness
D.C resistance
at 20ºC≤

Weight

in. mm AWG mm2 cmils Mpa psi kn mm Ω/1000ft Ω/km kg/km 1b/1000ft
0.2043 5.189 4 21.150 41740 703 102000 14.90 0.389 0.828 2.717 118.64 79.73
0.1880 4.775 4 17.908 35342 731 106000 13.09 0.358 0.978 3.209 100.46 67.51
0.1819 4.620 5 16.767 33090 758 110000 12.70 0.347 1.045 3.429 94.06 63.21
0.1729 4.392 5 15.150 29899 786 114000 11.91 0.329 1.156 3.793 84.99 57.12
0.1620 4.115 6 13.296 26240 786 118000 10.50 0.309 1.317 4.321 74.59 50.13
0.1549 3.934 6 12.155 23989 814 122000 9.89 0.295 1.441 4.728 68.19 45.83
0.1443 3,665 7 10.549 20820 841 126000 8.87 0.275 1.660 5.446 59.18 39.77
0.1369 3.477 7 9.495 18739 869 128000 8.25 0.261 1.845 6.053 53.27 35.80
0.1285 3.264 8 8.366 16510 883 128000 7.38 0.245 2.094 6.870 46.95 31.55
0.1144 2.906 9 6.633 13090 883 128000 5.85 0.218 2.642 8.668 37.20 25.00
0.1019 2.588 10 5.260 10380 883 128000 4.47 0.194 3.329 10.922 29.52 19.84
0.0907 2.304 11 4.170 8230 883 128000 3.68 0.173 4.203 13.79 23.38 15.71
0.0808 2.052 12 3.309 6530 883 128000 2.92 0.154 5.295 17.373 18.57 12.48

We are China High Carbon Aluminum Clad Wire / Single Acs Lightning Protection Wire manufacture and supplier,You can get more details with Email,you will get cheap price or factory price.

Tags: , ,

FAST AND RELIABLE SERVICE FOR YOUR PROJECT

Contact our trained experts today to find your perfect power solution.

ASK A QUESTION